Abstract

Rice husk ash (RHA) possesses high content of amorphous silica that is essential in pozzolanic reaction of supplementary cementing material (SCM) in concrete strength enhancement. However, usage of conventional RHA is unfavorable in current concrete industry. One of the reason that hindered the utilization of conventional RHA nowadays is due to its properties inconsistency namely chemical and mineralogical properties. In this regard, improvement on the RHA properties by introduction of chemical pretreatment prior to burning procedure is seen as an excellent way to reach the goal. In this research, raw rice husk was soaked in 0.1M hydrochloric acid (HCl) solution from one to three hours. After that, the pretreated rice husk was ground using planetary ball mill for 15 minutes. The effect of pretreatment soaking time to alkali metal removal and its chemical composition, mineralogical properties, particle size analysis as well as specific surface area of ultrafine treated rice husk ash (UFTRHA) were determined accordingly. As for alkali metal removal analysis, potassium element had the highest removal concentration with value of 55.35 mg/l. Meanwhile, amorphous silica content of the optimum sample was recorded as 96.00% at three hours of pretreatment soaking period. In terms of particle size and specific surface, it was also observed that, three hours of pretreatment soaking duration was sufficient to produce finest size of UFTRHA where d(0.1), d(0.5) and d(0.9) were obtained as 1.417µm, 4.493µm and 14.884µm respectively and the largest specific surface area of 196.61m2/g.